The amorphous indium gallium zinc oxide thin-film transistors (TFTs) with a multilayer high-k gate stack are investigated in this research. In order to achieve a high quality gate insulator for plastic flexible display application, the multilayer high-k gate stacks (SiO2/TiO2/HfO2) are deposited by a low-temperature physical vapor deposition (PVD) process. On the other hands, an interfacial layer between the high-k stack and metal oxide channel is important for the device performance. The effects of interfacial layer material (SiO2 or Ga2O3) are also discussed in this report. The devices with SiO2 interfacial layer show a high on/off current ratio of similar to 7x10(7) for its low gate leakage current, a small sub-threshold swing of 0.093 V/decade and a high field-effect mobility of similar to 37.8 cm(2)/Vs for its good interface condition and low interface defeats. This research shows that the interface engineering of multilayer PVD gate stacks is necessary for oxide TFT fabrication.