This study reports about the use of Biochar derived from maple tree as a filler in Epoxy resin. Maple tree blocks were pyrolyzed in inert atmosphere at 600 degrees C and 1000 degrees C respectively and were characterized morphologically. The composite mechanical properties, i.e. stress-strain curves and related parameters (ultimate tensile strength, Young modulus, resilience, tensile toughness) were recorded as well as their friction coefficient. It is shown that at very low wt% of the filler, the Young modulus is increased while at higher wt% (2 wt% and above) the fragile behavior of the resin was converted in a ductile one, as elongation at break increased from 0.02 to 0.12. A huge impact of the filler is observed on tensile toughness as for the best sample is increased 11 times with respect with pure resin. A simple model able to describe the results and make predictions on other wt% is presented as well.