The structural-phase state of the contact zone and the factors that influence on the strength of diamond retention in the diamond carbide composites were determined. Composites were obtained by the new hybrid technology that eliminates the reheating of the metalized coating. The elaborated technology combines the thermal diffusion metallization of a diamond and the sintering by the scheme of self-dosed impregnation in a one-stage technological cycle. By the methods of electron microscopy, X-ray diffraction analysis, and Raman spectroscopy the structural and phase characteristics of the interphase boundary were investigated. The improvement of chemical and mechanical adhesion between the diamond and carbide matrix was obtained. It was shown that the specific productivity of the samples with a metalized diamond component is 39% higher than those without metallization. [GRAPHICS] .