In this study, cement mortars were modified with a commercial polymer admixture. The aim of this study is to investigate the influence of the polymer content on the mechanical and adhesion properties of the mortars and to relate these properties with mortars' microstructure. A series of mortars were produced with various polymer/cement/water/aggregate ratios. The adhesion properties of the mortars to clay bricks were tested with a simplified tensile testing measurement. The microstructure of mortars, as well as interfaces, were evaluated by Scanning Electron Microscopy (SEM). It was found that with high polymer content, large size hardened particles are formed, reducing the compressive strength of the mortars. Polymer addition enhances the adhesion between the mortar and brick. The mortar microstructure at the interface affects the adhesion properties and the mode of failure.