P2-type Fe/Mn-based oxides are considered as the competitive cathode materials for sodium-ion batteries because of high specific capacity and low material cost. However, it suffers from poor cycling stability and unsatisfactory rate capability. Herein, the lithium-doped Na0.67Li0.1Fe0.4Mn0.5O2 microspheres are successfully synthesized via a three-step method. Benefiting from the synergetic effect of the double modification through the morphology controlling and lithium doping, the Na0.67Li0.1Fe0.4Mn0.5O2 delivers an improved cycling stability and rate performance. Moreover, fluorine is successfully introduced to further improve the electrochemical performance of the Na0.67Li0.1Fe0.4Mn0.5O2. Fluorine doping can boost the stability of the material crystal structure because of the strong electronegativity of fluorine and the stable fluorine-metal bond. Meanwhile, fluorine doping avoids the formation of extra O3 phase by reducing the average valence of transition metals. Most importantly, P2-type 10 mol% F-Na0.67Li0.1-Fe0.4Mn0.5O2 shows a high discharge specific capacity of 182.0 mAh g(-1) at 20 mA g(-1), excellent capacity retention of 90.0% after 50 cycles and outstanding rate performance of 128.7 mAh g(-1) at 400 mA g(-1). Apparently, such a modification strategy apparently promotes the electrochemical performances of the P2-type Fe/Mn-based oxide and increases the commercial application possibilities of this cathode material in sodium-ion batteries. (C) 2019 Elsevier Ltd. All rights. reserved.