Preparation of Rb-beta -alumina was realized by the gel-to-crystallite conversion method. Reaction of hydrated aluminum hydroxide gel with RbOH in ethanol medium gave rise to the Rb+-inserted pseudoboehmite precursor under wet chemical conditions. The thermal decomposition of the precursor yielded Rb-beta -alumina. The Rb2O:Al2O3 ratio of monophasic Rb-beta -alumina ranged from 1:10 to 1:22. The extended stability in the compositional range is due to the fact that the conduction planes containing Rb+ and O2- ions can have lower occupancy of Rb+ ions for larger sized alkali ions, permitting the steric separation of the adjoining spinel blocks. High-resolution electron microscopy revealed that the decreasing occupancy of alkali ions in the conduction plane is balanced by changing widths of spinel blocks arising from the shift of tetrahedral Al3+ ions to octahedral sites and an accompanying increase in stacking defects.