A major challenge for longer life lithium ion batteries is the irreversible loss of active lithium during the first charge/discharge cycles, which consequently reduces the practical energy density in cells without lithium ion excess. This degradationmechanism is especially detrimental for high-capacity anodes with low first cycle Coulombic efficiency. The present study aims for overcoming this challenge by pre-lithiating the high-voltage spinel LiNi0.5Mn1.5O4 (LNMO) positive electrode material with a simple and easily scalable chemical process via stirring LNMO particles with Li metal in boiling pentanol. The subsequent structural and electrochemical analysis proves the electrochemical accessibility of the "extra" lithium and long-term cycling stability. Charging/discharging the material in LNMO parallel to graphite (C) and LNMO parallel to silicon/carbon (Si/C) cells demonstrates positive effects on discharge capacity, energy and capacity retention. Furthermore, the additional active lithium is used to increase the specific capacity of the cells by including the lower potential region of LNMO through application of a lower cell cutoff voltage of 2.4 V. Comparing "standard" LNMO parallel to C with pre-lithiated LNMO parallel to Si/C cells (both charged/discharged at standard cutoff voltages of 3.0 and 4.95 V), improvements in specific energy of >21% can be identified. (C) The Author(s) 2019. Published by ECS.