C-60 films, prepared by solution casting, were studied by means of in situ probe beam deflection (PBD) combined with cyclic voltammetry (CV). PBD is a powerful technique for investigation of phenomena at the electrode/electrolyte interface in acetonitrile with quaternary ammonium and alkali metal salts as supporting electrolytes. In tetra-n-butylammonium (TBA(+)) salt solution, a stable CV can be obtained during the first two reduction/reoxidation waves. On reduction, injection of cations to maintain charge balance and dissolution of small amount of C-60(-) (TEA(+)) and/or C-60(2-) (TBA(+))(2) are detected. During the reoxidation process ejection of cations and injection of anions occur simultaneously, especially for the second reoxidation wave. In the case where TBABr is the supporting electrolyte, the accompanied behavior is more complicated than in TBABF(4), TBAClO(4), and TBAPF(6) solutions. A small pair of prewaves in CV are proposed due to oxidation/reduction of C-60 domains but not dissolution/redeposition of C-60 film. Extending the potential scan range to the third reduction wave, no apparent corresponding reoxidation wave is related to the third reduction wave, the electroactivity of the film disappears rapidly and dissolution of C-60 film is observed. In tetraethylammonium (TEA(+)) and NAClO(4) solutions, the electrochemistry of the C-60 films is unstable, and potential scans lead to dissolution of flaking of the film.