Carbonized zeolitic imidazolate frameworks (ZIFs) show potential as mesoporous heterogeneous catalysts with high metal loadings. ZIF-67 and ZIF-8 were used to create mono- and bimetallic CoCu particles supported on nitrogen-doped carbon via self-assembly in methanol at room temperature, followed by carbonization at 675 degrees C. A Cu precursor, Cu(NO3)(2)center dot 2H(2)O, was impregnated into the ZIF-67 before carbonization to obtain bimetallic catalysts. Nanoalloy particles with different CoCu ratio were synthesized and characterized using XRD. The materials were further characterized using TEM, SEM, XRF and nitrogen physisorption. The different alloys were tested in conversion of cyclohexanone to the corresponding silyl ether. Complete conversion of cyclohexanone at 90 degrees C for 24 h were obtained. The catalyst Co99Cu1@NC gave a 60% increase in yield over a pure Co analogue. Graphic