The nanoparticles of Mn-1.5[Cr(CN)(6)]center dot mH(2)[email protected][Cr(CN)(6)]center dot nH(2)O core-shell prussian blue analogues (PBA) embedded with carbon additives (PBA-C) were synthesized and characterized as electrode material for solid state battery application. The impedance spectroscopy and cyclic voltametry were used to study the electrochemical properties by adding functionalized carbon in 1:1 proportion to improve the electrical performance. The value of room temperature electrical conductivity of core-shell PBA and core-shell nanoparticles mixed with vulcan carbon (PBA-C) are found to be 1.574 x 10(-3) and 1.92 x 10(-3) Scm(-1), respectively. Using Li2La3Zr2O12 (LZZO) electrolyte, single cell was fabricated with PBA-C material, and studied its charging-discharging cycles, which exhibits higher current density with stable performance for 400 cycles for time slots of 400 min. The study reveals that the PBA core-shell nanoparticles mixed with carbon (PBA-C) may be a potential candidate as an electrode material in the form of a single cell using LZZO electrolyte. (C) 2020 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.