Journal of Industrial and Engineering Chemistry, Vol.93, 322-332, January, 2021
DOI10.1016/j.jiec.2020.10.008  Export Citation
A porous multifunctional and magnetic layered graphene oxide/3D mesoporous MOF nanocomposite for rapid adsorption of uranium(VI) from aqueous solutions
Asma Amini1, Mostafa Khajeh1, †, Ali Reza Oveisi1, Saba Daliran1, 2, Mansour Ghaffari-Moghaddam1, and Hojat Samareh Delarami1
  • 1Department of Chemistry, Faculty of Science, University of Zabol, Zabol, Iran
  • 2Faculty of Chemistry, Bu-Ali Sina University, Hamedan, Iran
E-mail:
A novel adsorbent, GO/Fe3O4/OPO3H2/PCN-222, was successfully synthesized via graphene oxide (GO) modification with magnetic particles, phosphorous-containing groups, and a mesoporous Zr-MOF, PCN-222 (PCN stands for Porous Coordination Network), respectively, to give the nominal composite. The last step was through a solvent-assisted ligand incorporation technique. Morphological, structural, and physicochemical properties of the hybrid material was assessed by FT-IR, PXRD, SEM/EDX, BET surface area, VSM, TGA/DSC, UV-vis DRS, and ICP-OES analyses. This solid was then used for dispersive solid phase extraction of uranium ions dissolved in water. Several parameters including pH of solution, extraction and desorption times, amount of adsorbent, and type and concentration of elution solvent were investigated and optimized. The maximum adsorption capacity of adsorbent was found to be 416.7 mg g-1 (pH, 6.2; amount of adsorbent, 5.0 mg; extraction time, 3.0 min) beyond what was achievable with the individual components. In addition, various coordination modes between the multifunctional adsorbent and uranyl ions were investigated by DFT calculations in details, revealing some favorable non-covalent cation-π interaction and strong binding of free-base porphyrin, carboxyl and phosphorous-containing groups to the uranium ions. Under optimized conditions, high determination coefficient (R2 = 0.9994) was obtained and limit of detection and relative standard deviation were found 0.9 μg L-1 and 2.7%, respectively.
Keywords:Mesoporous metal-organic framework;MOF-545;PCN-222;MOF-derived materials;Uranium ions;Magnetic solid phase extraction;Water treatment
  1. Safaei M, Foroughi MM, Ebrahimpoor N, Jahani S, Omidi A, Khatami M, Trends Anal. Chem., 118, 401 (2019)
  2. Vaitsis C, Sourkouni G, Argirusis C, Ultrason. Sonochem., 52, 106 (2019)
  3. Masoomi MY, Morsali A, Dhakshinamoorthy A, Garcia H, Angew. Chem.-Int. Edit., 58, 15188 (2019)
  4. Dhakshinamoorthy A, Li Z, Garcia H, Chem. Soc. Rev., 47, 8134 (2018)
  5. Ghaleno MR, Ghaffari-Moghaddam M, Khajeh M, Oveisi AR, Bohlooli M, J. Colloid Interface Sci., 535, 214 (2019)
  6. Oudi S, Oveisi AR, Daliran S, Khajeh M, Teymoori E, J. Colloid Interface Sci. (2019).
  7. Gandara-Loe J, Ortuno-Lizaran I, Fernandez-Sanchez L, Alio JL, Cuenca N, Vega-Estrada A, Silvestre-Albero J, ACS Appl. Mater. Interfaces, 11, 1924 (2019)
  8. Jia Q, Li Z, Guo C, Huang X, Song Y, Zhou N, Wang M, Zhang Z, He L, Du M, Nanoscale, 11, 20956 (2019)
  9. Kahkha MRR, Oveisi AR, Kaykhaii M, Kahkha BR, Chem. Cent. J., 12, 77 (2018)
  10. Wen M, Li G, Liu H, Chen J, An T, Yamashita H, Environ. Sci. Nano, 6, 1006 (2019)
  11. Tang Y, Dubbeldam D, Guo X, Rothenberg G, Tanase S, ACS Appl. Mater. Interfaces, 11, 21126 (2019)
  12. Xie Y, Chen C, Ren X, Tan X, Song G, Chen D, Alsaedi A, Hayat T, J. Colloid Interface Sci., 55, 117 (2019)
  13. Lv ZM, Wang HY, Chen CL, Yang SM, Chen L, Alsaedi A, Hayat T, J. Colloid Interface Sci., 537, A1 (2019)
  14. Wang Q, Astruc D, Chem. Rev., 120, 1438 (2019)
  15. Li S, Huo F, Nanoscale, 7, 7482 (2015)
  16. Li S, Yang K, Tan C, Huang X, Huang W, Zhang H, Chem. Commun., 52, 1555 (2016)
  17. Muschi M, Serre C, Coord. Chem. Rev., 387, 262 (2019)
  18. Zhang N, Qi WX, Huang LL, Jiang E, Bao JJ, Zhang XP, An BG, He GH, Chin. J. Chem. Eng., 27(6), 1348 (2019)
  19. Liu X, Sun J, Xu XT, Alsaedi A, Hayat T, Li JX, Chem. Eng. J., 360, 941 (2019)
  20. Miri MG, Khajeh M, Oveisi AR, Bohlooli M, Spectroc. Acta Pt. A-Molec. Biomolec. Spectr., 205, 200 (2018)
  21. Liu X, Xu XT, Sun J, Alsaedi A, Hayat T, Li JX, Wang XK, Chem. Eng. J., 343, 217 (2018)
  22. Navalon S, Dhakshinamoorthy A, Alvaro M, Antonietti M, Garcia H, Chem. Soc. Rev., 46, 4501 (2017)
  23. Wang M, Niu Y, Zhou J, Wen H, Zhang Z, Luo D, Gao D, Yang J, Liang D, Li Y, Nanoscale, 8, 14587 (2016)
  24. Khajeh M, Sharifirad M, Bohlooli M, Ghaffari-Moghaddam M, RSC Adv., 6, 54702 (2016)
  25. Hemmati M, Rajabi M, Asghari A, Microchim. Acta, 185, 160 (2018)
  26. Duan SX, Xu XT, Liu X, Wang YN, Hayat T, Alsaedi A, Meng YD, Li JX, J. Colloid Interface Sci., 513, 92 (2018)
  27. Xie Y, Chen CL, Ren XM, Wang XX, Wang HY, Wang XK, Prog. Mater. Sci., 103, 180 (2019)
  28. Turick CE, Berry CJ, J. Environ. Radioact., 151, 12 (2016)
  29. Fan S, Cao B, Deng N, Hu Y, Li M, J. Hazard. Mater., 379, 120570 (2019)
  30. Shah F, Soylak M, Kazi TG, Afridi HJ, J. Radioanal. Nucl. Chem., 296, 1239 (2013)
  31. Soylak M, Khan M, Alosmanov R, Shah J, Jan MR, J. Radioanal. Nucl. Chem., 308, 955 (2016)
  32. Zhu KR, Chen CL, Xu MWC, Chen K, Tan XL, Wakeel M, Alharbi NS, Chem. Eng. J., 331, 395 (2018)
  33. Song S, Yin L, Wang XX, Liu L, Huang SY, Zhang R, Wen T, Yu SJ, Fu D, Hayat T, Wang XK, Chem. Eng. J., 338, 579 (2018)
  34. Zhu KR, Chen CL, Wang HY, Xie Y, Wakeel M, Wahid A, Zhang XD, J. Colloid Interface Sci., 535, 265 (2019)
  35. Ling L, Zhang WX, J. Am. Chem. Soc., 137(8), 2788 (2015)
  36. Li B, Sun Q, Zhang Y, Abney CW, Aguila B, Lin W, Ma S, ACS Appl. Mater. Interfaces, 9, 12511 (2017)
  37. Gunathilake C, Gorka J, Dai S, Jaroniec M, J. Mater. Chem. A, 3, 11650 (2015)
  38. Carboni M, Abney CW, Liu S, Lin W, Chem. Sci., 4, 2396 (2013)
  39. Duan S, Wang Y, Liu X, Shao D, Hayat T, Alsaedi A, Li J, ACS Sustainable Chem. Eng., 5, 4073 (2017)
  40. Sarafraz H, Minuchehr A, Alahyarizadeh G, Rahimi Z, Sci. Rep., 7, 11675 (2017)
  41. Bai ZQ, Yuan LY, Zhu L, Liu ZR, Chu SQ, Zheng LR, Zhang J, Chai ZF, Shi WQ, J. Mater. Chem. A, 3, 525 (2015)
  42. Yang W, Bai ZQ, Shi WQ, Yuan LY, Tian T, Chai ZF, Wang H, Sun ZM, Chem. Commun., 49, 10415 (2013)
  43. Luo BC, Yuan LY, Chai ZF, Shi WQ, Tang Q, J. Radioanal. Nucl. Chem., 307, 269 (2016)
  44. Yuan L, Tian M, Lan J, Cao X, Wang X, Chai Z, Gibson JK, Shi W, Chem. Commun., 54, 370 (2018)
  45. Yang P, Liu Q, Liu J, Zhang H, Li Z, Li R, Liu L, Wang J, J. Mater. Chem. A, 5, 17933 (2017)
  46. Li L, MA W, Shen S, Huang H, Bai Y, Liu H, ACS Appl. Mater. Interfaces, 8, 31032 (2016)
  47. Huang SY, Pang HW, Li L, Jiang SB, Wen T, Zhuang L, Hu BW, Wang XK, Chem. Eng. J., 353, 157 (2018)
  48. Yin L, Hu B, Zhuang L, Fu D, Li J, Hayat T, Alsaedi A, Wang X, Chem. Eng. J., 381, 122744 (2020)
  49. Yu S, Wei D, Shi L, Ai Y, Zhang P, Wang X, Environ. Pollut., 251, 975 (2019)
  50. Pang H, Huang S, Wu Y, Yang D, Wang X, Yu S, Chen Z, Alsaedi A, Hayat T, Wang X, Inorg. Chem. Front., 5, 2399 (2018)
  51. Wu Y, Li B, Wang X, Yu S, Pang H, Liu Y, Liu X, Wang X, Chem. Eng. J., 378, 122105 (2019)
  52. Yin L, Hu YZ, Ma R, Wen T, Wang XX, Hu BW, Yu ZM, Hayat T, Alsaedi A, Wang XK, Chem. Eng. J., 359, 1550 (2019)
  53. Pang HW, Diao ZF, Wang XX, Ma Y, Yu SJ, Zhu HT, Chen ZS, Hu BW, Chen JR, Wang XK, Chem. Eng. J., 366, 368 (2019)
  54. Zhong X, Liang W, Lu Z, Hu B, Appl. Surf. Sci., 504, 144403 (2020)
  55. Yang S, Li Q, Chen L, Chen Z, Hu B, Wang H, Wang X, Chem. Eng. J., 385, 123909 (2020)
  56. Yao W, Wu Y, Pang H, Wang X, Yu S, Wang X, Sci. China Chem., 61, 812 (2018)
  57. Ozdemir S, Oduncu MK, Kilinc E, Soylak M, Environ. Radioact., 171, 217 (2017)
  58. Wang D, Xu YB, Xiao DF, Qiao QG, Yin P, Yang ZL, Li JX, Winchester W, Wang Z, Hayat T, J. Hazard. Mater., 371, 83 (2019)
  59. Di T, Tan DG, Yu Q, Lin JW, Zhu TT, Li TS, Li L, Langmuir, 35(43), 13860 (2019)
  60. Fotovat H, Khajeh M, Oveisi AR, Ghaffari-Moghaddam M, Daliran S, Microchim. Acta, 185, 469 (2018)
  61. Dhakshinamoorthy A, Asiri AM, Garcia H, Adv. Mater., 31, 190061 (2109)
  62. Liu Y, Chin. J. Chem. Eng., 27(6), 1257 (2019)
  63. Karagiaridi O, Bury W, Mondloch JE, Hupp JT, Farha OK, Angew. Chem.-Int. Edit., 53, 4530 (2014)
  64. Deria P, Bury W, Hod I, Kung CW, Karagiaridi O, Hupp JT, Farha OK, Inorg. Chem., 54(5), 2185 (2015)
  65. Dormond A, Belkalem B, Charpin P, Lance M, Vigner D, Folcher G, Guilard R, Inorg. Chem., 25, 4785 (1986)
  66. Feng D, Gu ZY, Li JR, Jiang HL, Wei Z, Zhou HC, Angew. Chem.-Int. Edit., 51, 10307 (2012)
  67. Morris W, Volosskiy B, Demir S, Gandara F, McGrier PL, Furukawa H, Cascio D, Stoddart JF, Yaghi OM, Inorg. Chem., 51(12), 6443 (2012)
  68. Ghaleno MR, Ghaffari-Moghaddam M, Khajeh M, Oveisi AR, Bohlooli M, J. Colloid Interface Sci., 535, 214 (2019)
  69. Hummers WS, Offeman RE, J. Am. Chem. Soc., 80, 1339 (1958)
  70. Zhou C, Wu H, Wang M, Huang C, Yang D, Jia N, Mater. Sci. Eng. C-Biomimetic Supramol. Syst., 78, 817 (2017)
  71. Liu Y, Moon SY, Hupp JT, Farha OK, ACS Nano, 9, 12358 (2015)
  72. Becke AD, J. Chem. Phys., 98, 5648 (1993)
  73. Frisch MJ, Trucks GW, Schlegel HB, Scuseria GE, Robb MA, Cheeseman JR, et al., Gaussian 09 Rev. A.02, Wallingford, CT, (2009).
  74. Chiodo S, Russo N, Sicilia E, J. Chem. Phys., 125, 104107 (2006)
  75. Biegler-Konig F, Schonbohm J, Bayles D, J. Comput. Chem., 22, 545 (2001)
  76. Glendening ED, Reed AE, Carpenter JE, Weinhold F, NBO Version 3.1, Gaussian Inc., Pittsburgh, 2003.
  77. Zhang T, Zhu GY, Yu CH, Xie Y, Xia MY, Lu BY, Fei X, Peng Q, Microchim. Acta, 186, 207 (2019)
  78. Shah J, Jan MR, Carbohydr. Polym., 199, 461 (2018)
  79. Oveisi AR, Delarami HS, Khajeh M, Mirjahanshahi S, Haghani A, Daliran S, Ghaffari-Moghaddam M, J. Mol. Struct., 1204, 127559 (2020)