The use of organic radicals as building blocks is an effective approach to the production of open-shell coordination polymers (CPs). Two-dimensional (2D) CPs with honeycomb spin-lattices have attracted attention because of the unique electronic structures and physical properties afforded by their structural topology. However, radical-based CPs with honeycomb spin-lattices tend to have low chemical stability or poor crystallinity, and thus novel systems with high crystallinity and persistence are in strong demand. In this study, a novel triangular organic radical possessing three pyridyl groups, tris(3,5-dichloro-4-pyridyl)methyl radical (trisPyM) was prepared. It exhibits luminescence, high photostability, and a coordination ability, allowing formation of defined and persistent 2D CPs. Optical measurements confirmed the luminescence of trisPyM both in solution and in the solid state, with emission wavelengths, lambda(em), of 665 and 700 nm, respectively. trisPyM exhibits better chemical stability under photoirradiation than other luminescent radicals: the half-life of trisPyM in CH2Cl2 was 10 000 times that of the tris(2,4,6-trichlorophenyl)methyl radical (TTM), a conventional luminescent radical. Complexation between trisPyM and Zn-II (hfac)(2) yielded a single crystal of a 2D CP trisZn, possessing a honeycomb lattice with graphene-like spin topology. The coordination structure of trisZn is stable under evacuation at 60 degrees C. Moreover, trisZn exhibits luminescence at 79 K, with lambda(em) = 695 nm, and is a rare example of a luminescent material among 2D radical-based CPs. Our results indicate that trisPyM may be a promising building block in the construction of a new class of 2D honeycomb CPs with novel properties, including luminescence.