This work aims to develop hydrogel films of starch and carboxymethyl cellulose (CMC) crosslinked with sodium trimetaphosphate (STMP) and to characterize some of their properties. Starch and STMP (S/T), starch and CMC (S/C), and mixed (S/T/C) films were prepared by casting. The degree of substitution, morphology, swelling degree, FTIR, mechanical properties, and sorption isotherms were studied. Reticulated samples (S/T and S/T/C) showed the same degree of substitution (0.050 +/- 0.001). All films presented homogeneous morphology, but the mixed film showed greater roughness. Crosslinking increased the swelling capacity of the mixed hydrogel at pH 7, although it remained decreased concerning the S/T hydrogel. However, this property was sensitive to pH variations. The mixed film (S/T/C) showed greater mechanical resistance. The casting process was efficient to produce hydrogel films of starch/CMC crosslinked with STMP and the general results demonstrated the advantages of the mixed hydrogel.