In this study, 2,5-dichlorobenzophenone was synthesized as a monomer using 1,4-dichlorbenzene, and subsequently, copolymers of benzoyl-p-phenylene and p-phenylene were prepared. The average molecular weight was improved using the low-molecular- weight polymer cutting method. The average molecular weight and glass transition temperature of the synthesized polymers were estimated. The as-prepared polymer was used as a hard coating material, and the coating was conducted on a poly(methyl methacrylate) plate. Furthermore, physical properties of the coatings, such as pencil hardness, adhesive strength, and abrasion resistance, were estimated. As the amount of p-phenylene in the copolymer increased, pencil hardness and abrasion resistance improved. The amount of p-phenylene in the copolymer can be increased to 30 mol% in order to increase the hardness of the coating, and the adhesive strength was insufficient for the copolymers with p-phenylene ratio greater than 35 mol%.