Two series of thermotropic main chain discotic liquid crystalline polyethers, PR4m-n, based on rufigallol were prepared starting from the symmetric tetraethers of rufigallol, R4m; m and n represent the number of carbon atoms in the side chain and spacer segment, respectively. The symmetric tetraethers were in turn readily prepared by selective alkylation of rufigallol under controlled phase-transfer conditions. GPC analysis of the polymers suggested that they were all of moderate molecular weights, with M-n varying between 5400 and 17 000. The length of the spacer segment n in these polyethers was systematically varied, and its effect on the phase transition temperatures and the mesophase structure was examined using DSC, polarized light microscopy, and X-ray diffraction. It is noticed that when the spacer lengths are relatively long(n greater than or equal to 2m), the isotropization temperature (TD-i) decreases as the spacer length n increases, an observation that is in accordance with those previously made. However, when the spacer lengths are relatively small (n < 2m), the dependence of TD-i is quite the opposite; TD-i actually increases with an increase in spacer length. Furthermore, X-ray diffraction studies indicate that, in the discotic columnar mesophases that are formed, the columns pack in a hexagonal manner when n greater than or equal to 2m, while they do so in a rectangular lattice when n < 2m, leading to the formation of Dh and Dr mesophases, respectively. Finally, comparison of the discotic polyethers with their low molar mass analogues confirms the role of polymerization in stabilizing the mesophase; while all the polymers exhibit columnar mesophases, some of their low molar mass analogues are not liquid crystalline.