Materials Research Bulletin, Vol.31, No.9, 1141-1147, 1996
Lowering of Relaxor Transition-Temperature in Lead-Based Perovskites Under Pressure
The dielectric constants of lead iron niobate (PFN) and 40% lead zinc niobate (PZN) added to lead iron niobate (PFN0.6-PZN(0.4)) have been measured as a function of pressure up to 6 GPa under isothermal conditions between room temperature and 348 K. The relaxer transition temperature measured at 1 kHz excitation frequency varies at a rate -24.5 K/GPa for PFN and at a rate of - 28.8 K/GPa for the PFN0.6-PZN(0.4) composition.