The luminescence properties of Ce3+, Gd3+, and Tb3+ have been investigated in the compound CaAl2B2O7. The single excitation band peaking at about 320 nm and single emission band peaking at about 384 nm for Ce3+, without the characteristic doublet, are attributed to the extensive crystal-field splitting of 4f ground state. The emission of Gd3+ consists of well-known sharp lines and two weak bands around 319.5 and 325 nm. These bands are due to the coupling of Gd3+ with BO33- groups. The green emission of Tb3+ is considerably sensitized by Ce3+. Energy transfer from Ce3+ to Tb3+ in CaAl2B2O7 is efficient.