A novel dianhydride, 3,3＇-dioxo-[1,1＇]-spirodiphthalan-5,5＇,6,6＇-tetracarboxlic dianhydride, was synthesized and used as a monomer to prepare polyimides with several diamines via a conventional two-stage procedure. The intermediate poly(amic-acid)s had inherent viscosities of 0.84-1.71 dL/g and could be thermally converted into lightly yellow, transparent, flexible and tough films. Films cast from chemically imidized polyimides were transparent and colorless. The glass transition temperatures (Tg) were > 400 degrees C, and the 5% weight-loss temperatures were > 420 degrees C in N-2 and in air. The solubilities of these polyimides in various solvents were evaluated. The mechanical properties of some polyimides were also tested.