A new molecule-based weak ferromagnet of formula Fe[C6H5PO3]. H2O was synthesized It was characterized by thermogravimetric analysis and UV-visible and infrared spectroscopy, and the magnetic properties were studied using a superconducting quantum interference device magnetometer. The crystal structure of the compound was determined "ab initio" from X-ray powder diffraction data and refined by the Rietveld method. The crystals of Fe[C6H5PO3]. H2O are orthorhombic, space group Pmn2(1), with a = 5.668(8) Angstrom, b = 14.453(2) Angstrom, c = 4.893(7) Angstrom, and Z = 2. The title compound is isostructural with the previously reported lamellar M[C6H5PO3]. H2O, M = Mn(II), Zn(II), and Cd(II). The inorganic layers are made of Fe(II) ions octahedrally coordinated by dye phosphonate oxygen atoms and one from oxygen of the water molecule. These layers are then separated by bilayers of the phenyl groups, and van der Waals contacts are established between them. The refinement has shown that the phenyl rings are disordered in the lattice. The oxidation state of the metal ion is +2, and the electronic configuration is d(6) (S = 2) high-spin, as determined from de magnetic susceptibility measurements from 150 K to room temperature. Below 100 K, the magnetic moment of Fe[C6H5PO3]. H2O rises rapidly to a maximum at T-N = 21.5 K, and then it decreases again. The peak at T-N is associated with the 3D antiferromagnetic long-range ordering. Below the critical temperature, the title compound behaves as a "weak" ferromagnet, which represents the third type of magnetic materials characterized by having a finite zero-field magnetization, ferromagnets and ferrimagnets being the other two types. The large coercive field (i.e., 6400 G) observed in the hysteresis loop at T = 10 K is rare in molecule-based materials; it can be ascribed to a pronounced spin-orbit coupling for the T-5(2g) ground state of the Fe(II) ion in the octahedral environment.