Pd and Pd-Ag (24 wt.%) alloy composite membrane were prepared by electroless plating and magnetron sputtering, respectively. The membranes were characterized by scanning electron microscopy (SEM) and H-2 permeation measurement. Commercial microfiltration ceramic membrane were coated with gamma-Al2O3-based layer by the sol-gel method and used as substrate of Pd and Pd-Ag alloy film. Both the as-prepared membranes were shown: to be He gas-tight at room temperature with a thickness of <1 mu m. Permeation results showed that H-2 permeation through these composite membranes is mainly dominated by the surface chemistry of H-2 on or/and in the membranes. The membranes exhibited a high permeation rate of H-2 and a H-2/N-2 permselectivity of higher than 60 in the optimized operation conditions. (C) 2000 Elsevier Science B.V. All rights reserved.