The specific essential work of fracture, w(e), has been measured for a relatively thick walled uPVC pipe as a function of position through the wall of the pipe. w(e) was highest at the surface of the pipe and decreased significantly at the centre of the pipe wall. The variation in w(e) through the wall of the pipe correlated with the processing level of the uPVC material as measured by the critical temperature, T-c. The variability in the measured values of w(e) was substantially higher in the centre of the pipe where the processing levels were lower. This was likely to be a result of the variability in the microstructure of the material where poor processing had introduced regions of poor fusion of primary PVC particles.