The stress corrosion cracking (SCC) behavior of Al-brass and Cu10Ni alloys was investigated in 3.5% NaCl solution in absence and in presence of different concentrations of Na2S under open-circuit potentials using the constant slow strain rate technique. The results indicated that the Cu10Ni alloy is more susceptible to stress corrosion cracking than as-received Al-brass at strain rate of 3.5 x 10(-6) s(-1) in 3.5% NaCl in presence of high concentration of sulfide ions (1000 ppm). The sulfide ions (up to 500 ppm) has no effect on the stress corrosion cracking of the annealed Al-brass in 3.5% NaCl at two strain rates of 7.4 x 10(-6) and 3.5 x 10(-)6 s(-1.) The results support film rupture for Al-brass and sulfide stress corrosion cracking assisted with pitting corrosion for Cu10Ni at slip steps as the operating mechanisms.