An aluminosilicate glass matrix composite material reinforced by randomly oriented SiC-based (Tyranno(TM)) chopped fibres was fabricated. Slurry dipping and hot-pressing techniques were used to prepare dense composites containing 45 vol% fibres uniformly dispersed in the glass matrix. The mechanical properties and fracture mechanisms of the composite under flexion and compression loading were studied. In flexure, the composite showed higher modulus and strength than the unreinforced glass. However, in compression, the strength of the composite was lower than that of the monolithic glass. Considering the potential application of the material at high temperatures, the thermal aging behaviour of the composite in air at temperatures between 500 and 700 degreesC was investigated. The composite retained its room-temperature compressive strength after exposure for 26 h at 500 degreesC. The variation of compressive strength measured after exposures at higher temperatures was ascribed to mechanisms of fibre/matrix interface oxidation and to the softening of the glass matrix.