Journal of the Korean Industrial and Engineering Chemistry, Vol.14, No.3, 336-341, May, 2003
Export Citation
상용화제 SEBS-g-MA가 PA6/PP-g-MA 블렌드계의 나노 고차구조에 미치는 영향
Effects of Compatibilizer SEBS-g-MA on Nano-Mophology in Polyamide 6/Maleated Polypropylene Blends
고재송, 이창형1, †, 최형기2, 한애란2, 나재운3
  • 인하대학교 화학공학과, 인천 402-751
  • 1식품의약품안정청 의료기기평가부, 서울 122-704
  • 2기술표준원 생물화학기술표준부, 경기 427-716
  • 3순천대학교 고분자공학과, 전남 540-742
Jae-Song Koh, Chang Hyung Lee1, †, H.K. Choi2, Airan Hahn2, and Jae-Woon Nah3
  • Department of Chemical Engineering, Inha University, Inchon 402-751, Korea
  • 1Department of Medical Devices & Radiation Health, Korea Food & Drug Administraion, Seoul 122-704, Korea
  • 2Biotechnology & Environmental Engineering Division, Agency for Technology and Standards, Kyunggi-do 427-716, Korea
  • 3Department of Polymer Science and Engineering, Sunchon National University, Jeonnam 540-742, Korea
E-mail:
초록
Polyamide 6 (PA6)/maleated polypropylene (PP-g-MA) 블렌드계의 상용화제로 maleic anhydride (MA)가 그래프트 (graft)된 poly(styrene-b-ethylene-co-butylene-b-styrene) (SEBS-g-MA)를 첨가하여 블렌드의 고차구조에 미치는 영향을 small angle x-ray scattering, DSC 및 SEM을 이용하여 고찰하였다. SEBS-g-MA가 첨가된 시료는 첨가되지 않은 시료보다 PA6 분산상의 크기가 작았는데 이는 가공 또는 열처리 중 SEBS-g-MA의 무수말레산과 PA6의 아민 그룹(amine group) 사이에 반응이 일어나 PA6/PP-g-MA 계면에 PA6-SEBS-g-MA 그래프트 공중합체가 형성되어 이 공중합체가 상용화제로서 작용하여 계면장력을 안정화시켜 PA6 분산상 크기를 작게 한 것으로 추정되었다. 첨가된 SEBS-g-MA의 일부는 마이크로 상분리 (Micro-phase separation)되어 미세분산상으로 존재하게 되는데 그 크기는 첨가된 양이 많을수록, 저온보다 고온일수록 크다는 것이 관찰되었다. 미세분산상 SEBS-g-MA는 PP-g-MA 연속상의 결정화도를 낮추는 반면, PA6 분산상의 결정화도는 증가시켰다.
Effect of maleic anhydride grafted triblock copolymer of poly(styrene-b-ethylene-co-butylene-b-styrene) (SEBS-g-MA) on the morphology of the blends of polyamide 6 (PA6) and maleated polypropylene (PP-g-MA) was investigated by small angle x-ray scattering, differential scanning calorimeter and scanning electron microscopy. The size of the dispered PA6 decreased with addition of SEBS-g-MA. SEBS-g-MA reacted with the amine group of PA6 during the melt-compounding, and as a result, the copolymer, formed by interfacial reaction between PA6 and SEBS-g-MA, led to reduction in size of the dispersed PA6. SEBS-g-MA was partially microphase-separated to dispersion phase, and its size increased proportional to the amount of added SEBS-g-MA and increased temperature. The microphase-separated dispersion phase highly affected the crystallinity of the PP-g-MA matrix and PA6 dispersion.
Keywords:morphology;PA6;PP;SEBS-g-MA;small angle x-ray scattering
  1. Gonzalezmontiel A, Keskkula H, Paul DR, Polymer, 36(24), 4587 (1995) 
  2. Gonzalezmontiel A, Keskkula H, Paul DR, Polymer, 36(24), 4605 (1995) 
  3. Paul DR, Newman S, Polymer Blend, Academic Press, New York (1978)
  4. Han CD, Multiphase Flow in Polymer Processing, Academic Press, New York (1981)
  5. Ultracki LA, Polymer Alloys and Blends, Hanser, Munich (1989)
  6. Keith HD, Padden FJ, J. Appl. Phys., 35, 1270 (1964) 
  7. Keith HD, Padden FJ, J. Appl. Phys., 34, 2409 (1963) 
  8. Tanaka H, Nishi T, Phys. Rev., A, 39, 783 (1989) 
  9. Horiuchi S, Matchariyakul N, Yase K, Kitano T, Cho HK, Lee YM, Polymer, 37(14), 3065 (1996) 
  10. Horiuchi S, Matchariyakul N, Yase K, Kitano T, Choi HK, Lee YM, Polymer, 38(1), 59 (1997) 
  11. Horiuchi S, Matchariyakul N, Yase K, Kitano T, Choi HK, Lee YM, Polymer, 38(26), 6317 (1997) 
  12. Guinier A, Gournet G, Small-Angle Scattering of X-rays, John Wiley & Sons, Inc., London (1955)