The PAN-DMSO-Et4NBF4 and PAN-DMSO-Et4NTf (Tf is triflate ion) electrolytes were prepared as white, turbid foils with a thickness in the range of 0.1-0.5 mm, using the casting technique. Room temperature conductance of the electrolytes, detected from ac impedance experiments, was at the level of 8 and 14 mS cm(-1) for Et4NBF4 and Et4NTf salts, respectively. The electrochemical stability window of approximately 2.6-2.8 V was estimated using a glassy carbon electrode. Temperature dependence of the conductivity is of the Arrhenius-type for both electrolytes, with an activation energy of approximately 34 U mol(-1). The double-layer capacitors built with these electrolytes, serving both as separators and activated carbon powder (ACP) binders, showed a specific capacity of 50 F g(-1) of carbon material. Capacitors were assembled by sandwiching the PAN-DMSO-salt electrolyte between two PAN-salt-DMSO-ACP-AB electrodes and pressing across the system; the resulting devices had a coin-like shape with 8 mm diameter and thickness between 2.0 and 2.5 mm.