Several a-Si:H and a-Si:D films prepared by hot-wire chemical vapor deposition have been examined by small-angle neutron scattering (SANS) to search for H non-uniformity in this material. The SANS measurements were supplemented by small-angle X-ray scattering measurements. The differences in H/D detection sensitivity of these two techniques allow distinction of the scattering mechanisms. Two- or three-phase models are used to interpret the results quantitatively. Significant H non-uniformity, as well as a small fraction of microvoids, was found in the best-quality material. Samples grown with higher deposition rates or lower substrate temperatures have much larger void fractions. The size scale of the heterogeneity spans a range from 2 nm to more than 50 nm, with the largest features assigned to surface roughness. (C) 2003 Elsevier Science B.V All rights reserved.