LaMnxAl12-xO19 catalysts were prepared from NH4OH and metal nitrates solutions. Supercritical drying (SCD) and conventional oven drying (CD) methods were used to extract the water in the hydrogel. The effects of drying methods on properties of the catalysts were investigated by means of TEM, N-2-adsorption, thermogravimetry (TG)-differential thermal analysis (DTA) and X-ray diffraction. SCD method is beneficial to maintain high surface area and improving catalytic activity for methane combustion of the catalyst. The specific surface area and pore volume of LaMn1Al11O19 catalyst prepared by SCD method are 28 m(2)/g and 0.23 cm(3)/g, respectively, and the ignition of methane could be carried out at 450degreesC. However, those of the CD catalyst prepared from the same precursor are 15 m(2)/g, 0.11 cm(3)/g and 530 degreesC, respectively. Suitable Mn content (0 less than or equal to x less than or equal to 2) could promote the formation of LaMnAl11O19 hexaaluminate, while further addition of Mn (2 less than or equal to x less than or equal to 6) cause the formation of LaMnO3. (C) 2003 Elsevier B.V All rights reserved.