A new series of copolymers was synthesized through the oxidative polymerization of pyrrole (PY) and o-phenetidine (PHT) with inorganic oxidants in acidic media. The polymerization parameters including the mixing method of the oxidant with the comonomer, the comonomer ratio, the time, the temperature, the oxidant, the organic medium, and the acid were systematically optimized for the synthesis of copolymers with high yields, intrinsic viscosities, and solubility. The resultant copolymers were characterized by elemental analysis, infrared, ultraviolet-visible, solution high-resolution H-1 NMR and solid-state high-resolution C-13 NMR, circular dichroism spectroscopy, and cyclic voltammetry. The results showed that the PY observed content in the copolymers was much higher than the PY feed content. The regular variation of the polymerization yield, intrinsic viscosity, solubility, macromolecular structure, and electroactivity of the resulting polymers with the comonomer ratio, together with the complete solubility of a PY/PHT (10/90) polymer in highly polar solvents, indicated the formation of real random copolymers containing both PY and PHT units rather than a mixture of two homopolymers. However, the polymers containing more than 59 mol % PY were not homogeneous copolymers consisting of soluble and insoluble parts. A semiquantitative relationship between the polymerization yield or solubility of the copolymers and the polarity index of the organic solvents was examined. (C) 2004 Wiley Periodicals, Inc.