Isothermal crystallization and subsequent melting behavior for three different types of linear aromatic polyester, namely poly(ethylene terephthalate) (PET), poly(trimethylene terephthalate) (PTT), and poly(butylene terephthalate) (PBT), were investigated (with an emphasis on PTT in comparison with PET and PBT). These polyesters were different in the number of methylene groups (i.e. 2, 3, and 4 for PET, PTT, and PBT, respectively). Isothermal crystallization studies were carried out in a differential scanning calorimeter (DSC) over the crystallization temperature range of 182-208 degreesC. The wide-angle X-ray diffraction (WAXD) technique was used to obtain information about crystal modification and apparent degree of crystallinity. The kinetics of the crystallization process was assessed by a direct fitting of the experimental data to the Avrami, Tobin, and Malkin macrokinetic models. It was found that the crystallization rates of these polyesters were in the following order: PBT > PTT > PET, and the melting of these polyesters exhibited multiple-melting phenomenon. Lastly, the equilibrium melting temperature for these polyesters was estimated based on the linear and non-linear Hoffman-Weeks (LHW and NLHW) extrapolative methods. (C) 2003 Elsevier B.V. All rights reserved.