Germanium nanocrystals (12 nm mean diam) and amorphous thin films (60-250 nm thick) were prepared as anodes for lithium secondary cells. Amorphous thin film electrodes prepared on planar nickel substrates showed stable capacities of 1700 mAh/g over 60 cycles. Germanium nanocrystals showed reversible gravimetric capacities of up to 1400 mAh/g with 60% capacity retention after 50 cycles. Both electrodes were found to be crystalline in the fully lithiated state. The enhanced capacity, rate capability (1000C), and cycle life of nanophase germanium over bulk crystalline germanium is attributed to the high surface area and short diffusion lengths of the active material and the absence of defects in nanophase materials. (C) 2004 The Electrochemical Society.