초임계 상태에서 매크로에멀젼을 이용한 니켈 도금에 관한 연구
Studies on the Ni-Plating using Macroemulsion in Suppercritical State
박지영, 김재덕1, 이윤우2, 이창하3, 임종성4, †
  • 한국과학기술연구원 초임계유체국가지정연구실, 136-791 서울시 성북구 하월곡동 39-1
  • 1한국과학기술연구원 청정기술센터, 136-791 서울시 성북구 하월곡동 39-1
  • 2서울대학교 응용화학부, 151-742 서울시 관악구 신림동 산 56-1
  • 3연세대학교 화학공학과, 120-749 서울시 서대문구 신촌동 134
  • 4서강대학교 화공생명공학과, 121-742 서울시 마포구 신수동 1
Ji-Young Park, Jae Duck Kim1, Youn Woo Lee2, Chang Ha Lee3, and Jong Sung Lim4, †
  • National Research Laboratory for Supercritical Fluid, KIST, 39-1, Hawolgok-dong, Sungbuk-gu, Seoul 136-791, Korea
  • 1Clean Technology Research Center, KIST, 39-1, Hawolgok-dong, Sungbuk-gu, Seoul 136-791, Korea
  • 2School of Chemical Engineering and Institute of Chemical Processes, Seoul National University, San 56-1, Shilin-dong, Gwanak-gu, Seoul 151-742, Korea
  • 3Department of Chemical Engineering, Yonsei University, 134, Sinchon-dong, Seodaemun-gu, Seoul 120-749, Korea
  • 4Department of Chemical Engineering, Sogang University, 1, Shinsu-dong, Mapo-gu, Seoul 121-742, Korea
E-mail:
초록
본 연구는 초임계 이산화탄소를 사용한 전해 도금 공정으로 계면활성제에 의해 니켈 도금액과 이산화탄소간에 매크로에멀젼을 형성시키고, 그 용액내에서 구리 위에 니켈을 도금시키는 방법이다. 매크로에멀젼 형성에 있어서 가장 중요한 요소인 계면활성제로 친이산화탄소기와 친수기를 동시에 지닌 fluorocarbon-hydrocarbon계 sodium salt of bis (2,2,3,3,4,4,5,5-octafluoro-1-pentanol) sulfosuccinate (F_AOT)를 합성하였고, 이것의 이산화탄소에 대한 용해도를 측정하였다. 최적의 도금 조건에서 도금액과 이산화탄소의 매크로에멀젼을 형성시켜 도금을 수행하였고 그 결과, 기존의 도금액에 비해 도금액을 1/2가량 절감할 수 있었다. 도금 수행 후, 도금 제품에 대한 품질 평가는 외관, 도금 두께, 도금 균일성 등을 통해 이루어졌으며, 상압에서 실시된 기존의 방법을 통해 얻어진 결과와 비교하였다.
This is the method that Ni+2 in macroemulsion have deposit in Cu substrate after Ni-plating solution/scCO2 emulsion using the surfactant was formed. For the formation of emulsion, we synthesized fluorocarbon-hydrocarbon hybrid surfactants, in that, sodium salt of bis (2,2,3,3,4,4,5,5-octafluoro-1-pentanol) sulfosuccinate which has both ‘CO2 philic’ chains and ‘hydrophilic’ head group. The plating solution could be reduced to 1/2 times by this new electroplating method. Quality of plated ware was evaluated by using the brilliance, the uniformity on surface of plated ware, and the plating thickness. Plated wares were compared between the results in supercritical condition and that in atmospheric condition.
Keywords:Macroemulsion;Ni-Plating;Cu Substrate;Bis(2,2,3,3,4,4,5,5-octafluoro-1-pentanol) Sulfosuccinate
  1. Yoshida H, Sone M, Mizushima A, Abe K, Tao XT, Ichihara S, Miyata S, Chem. Lett., 11, 1086 (2002) 
  2. Park JY, Jin HS, Lee YW, Lim JS, "Interfacial Tension between scCO2 and Nickel-Plating Solution with Anionic Surfactant," Proceedings of 1st International Symposium on Supercritical Fluid Technology for Energy and Environment Applications, 251 (2002)
  3. Lee SW, Sewha, 191 (1991)
  4. Liu ZT, Erkey C, Langmuir, 17(2), 274 (2001) 
  5. Eastoe J, Nave S, Downer A, Paul A, Rankin A, Tribe K, Penfold J, Langmuir, 16(10), 4511 (2000) 
  6. Kim HW, Jin YW, Park KH, Kim HD, Yoon BH, Wai CM, "Metal Nanoparticle Synthesis and its Catalytic Organic Reactions in Water-in-CO2 Microemulsion using Fluorinated AOT", Proceedings of 1st International Symposium on Supercritical Fluid Technology for Energy and Environment Applications, 383 (2002)
  7. Byun HS, Hasch BM, McHugh MA, Fluid Phase Equilib., 115(1-2), 179 (1996)