The effects of support and additive on the oxidation state and catalytic activity of Pt catalyst in the low temperature propane combustion were systematically investigated on Pt/MgO, Pt/Al2O3 and Pt/SiO2-Al2O3. The catalytic activity varied much with both support materials and additives. The catalyst on the more acidic support showed higher activity, and the catalytic activity on every support materials increased as the electronegativity of additives increased, while some additives decreased the activity. The oxidation state of platinum, estimated by white line intensity of Pt L-III-edge XANES spectrum, also varied with the support and additives, and additives with higher electronegativity greatly prevented the platinum from its oxidation under oxidising atmosphere. Among almost all the catalysts with various supports and various additives, a clear relationship was observed between the oxidation state of platinum and the catalytic activity; the more metallic platinum showed higher activity. Thus, it was concluded that the total electrophilic/electrophobic property derived from those of the support and additive controls the oxidation state of platinum, which intensively affects the catalytic activity; i.e. higher electrophilic property provides less oxidised platinum, resulting in high catalytic activity. The mechanism of this effect was also discussed on the basis of thermochemical data, and it was proposed that the electrophobic materials promote the noble metal oxidation since the noble metal oxo-anion such as PtOalphadelta- is more stabilised with electrophobic cation. (C) 2003 Elsevier B.V. All rights reserved.