Epoxide and aldehyde end-functionalized poly(ethylene glycol)s (PEGS) (M-w = 400, 1000, 3400, 5000, and 20,000) were grafted to poly(ethylene terephthalate) (PET) film substrates that contained amine or alcohol groups. PET-PAH and PET-PEI were prepared by reacting poly(allylamine) (PAH) and polyethylenimine (PEI) with PET substrates, respectively; PET-PVOH was prepared by the adsorption of poly(vinyl alcohol) (PVOH) to PET substrates. Grafting was characterized and quantified by the increase of the intensity of the PEG carbon peak in the X-ray photoelectron spectra. Grafting yield was optimized by controlling reaction parameters and was found to be substrate-independent in general. Graft density consistently decreased as PEG chain length was increased. This is likely due to the higher steric requirement of higher molecular weight PEG molecules. Water contact angles of surfaces containing long PEG chains (3400, 5000, and 20,000) are much lower than those containing shorter PEG chains (400 and 1000). This indicates that longer PEG chains are more effective in rendering surfaces hydrophilic. Protein adsorption experiments were carried out on PET- and PEG-modified derivatives using collagen, lysozyme, and albumin. After PEG grafting, the amount of protein adsorbed was reduced in all cases. Trends in surface requirements for protein resistance are: surfaces with longer PEG chains and higher chain density, especially the former, are more protein resistant; PEG grafted to surfaces containing branched or network polymers is not effective at covering the underlying substrate, and thus does not protect the entire surface from protein adsorption; and substrates containing surface charge are less protein-resistant. (C) 2004 Wiley Periodicals, Inc.