New crosslinked cellulose-based plastic films were synthesized with olefin metathesis as a crosslinking reaction. Microcrystalline cellulose was first dissolved in a lithium chloride/N,N-dimethylacetamide solvent system and acylated by omega-undecenoyl chloride under microwave irradiation with N,N-dimethyl-4-aminopyridine as the catalyst. Cellulose unsaturated fatty acyl esters with a degree of substitution (DS) ranging from 1.4 to 2.0 were then crosslinked by olefin metathesis with a first generation Grubbs catalyst. Crosslinking ratios (T) ranging from 20 to 90% were obtained for low catalyst amounts (<1.2%), but gels appeared when T was too high. To avoid this gel formation, cellulose was acylated with a mixture of lauroyl and omega-undecenoyl chlorides. This internal dilution allowed us to obtain films of every case and various T (varying from 10 to 80% for a catalyst amount below 3.5%). Plastics were characterized by Fourier transform infrared (FTIR) spectroscopy, and the fatty acid mixture resulting from the hydrolysis of cellulose esters were analyzed by gas chromatography (GC) and NMR spectroscopy. Mechanical properties showed that the elastic modulus and tensile failure stress was higher when the plastic films were crosslinked. (C) 2004 Wiley Periodicals, Inc.