The surface of lanthanide(III)-doped LaPO4 nanoparticles was modified by reaction with an alcohol, leading to a covalent bond between the ligand and the particle surface. The surface of lanthanide(III)doped LaF3 nanoparticles was modified to alter the solubility of the nanoparticles and study the influence of surface effects on the luminescence of lanthanide ions doped in the nanoparticles. The coordinated organic ligands can be modified by a quantitative exchange reaction in solution or by using functionalized ligands during the synthesis. Variation of the ratio of ligand to core reagents had a significant influence on the size of the nanoparticles. Smaller nanoparticles were formed with a higher ligand ratio. The optical properties of these nanoparticles show a strong dependence on nanoparticle size, indicating the influence of quenching probably by CH and OH groups at or near the surface of the nanoparticle cores. The luminescence lifetime of LaF3/Eu nanoparticles varied from 6.5 to 7.4 ms for nanoparticles with an average size of 7.1 to 8.4 nm. A significant reduction of the quenching from the surface of the nanoparticles was obtained by the synthesis of coreshell nanoparticles, in which a shell of LaF(sub)3 was grown epitaxially around the doped core nanoparticles. This leads to an increase in the luminescence lifetime of the EU3+ ion and the observation of emissions from the D-5(2) energy level, in addition to emissions from the 51), and D-5(0) levels. The quantum yield of LaF3/Ce,Tb nanoparticles could be increased from 24 to 54% by the growth of a LaF3 shell around