Semi-interpenetrating polymer networks (SIPNs) and polymer mixtures (1: 1 mass ratio) based on segmented polyester polyurethane (PU) with carboxylic groups and methacrylic copolymer (PM) with tertiary amine groups were studied by the electron spin resonance (ESR) spin label method. The concentration of functional groups varied from 0 to 0.45 mmol g(-1) in both prepolymers. The ESR spectra of spin labelled PM component were used to characterise the heterogeneity of segmental motion and transitions due to the additional polyrner interactions imposed by complementary functional groups. The results were deduced from the temperature dependent ESR spectra. Two component spectra reflect the effect of PU chains on segmental motion of the PM component below the macroscopic glass transition temperature, T-g. The ratio of the fast and slow component was related to the complex polymer-polymer interaction or extent of miscibility. Restrictions of segmental motion of PM chains increase with functional groups concentration and above certain concentration (0.25 mmol g(-1)) PM segments in the network assess faster motion suggesting a change in the local packing density and domain structure. An increased miscibility and disorganisation of the ordered domains are confirmed by the loss of spherulitic morphology and crystallinity at higher functional groups concentration. PU/PM mixtures reveal similar motional behaviour as SIPNs of the same composition. However, the differences in the fractional amount of fast and slow motions confirm better interpenetration and interaction of the two polymers in the SlPNs. The results of motional heterogeneity and polymer interactions were complemented with the T(g)s. (C) 2004 Elsevier Ltd. All rights reserved.