Ordered silicas with large (9-15 nm), uniform, cagelike mesopores were synthesized under acidic aqueous conditions from tetraethyl orthosilicate in the presence of sodium chloride using poly(ethylene oxide)-poly(butylene oxide)-poly(ethylene oxide) triblock copolymer B50-6600 (EO39BO47EO39, Dow Chemicals) as a supramolecular template. Except for the use of NaCl in our case, the synthesis mixture composition was the same as that originally reported by Zhao et al. for the synthesis of FDU-1 silica, which was later shown to exhibit a cubic close-packed (Fm3m) structure with stacking faults related to the occurrence of hexagonal close-packed stacking sequences. The copolymer-templated silicas were formed at room temperature and in most cases were subjected to the hydrothermal treatment at 373 or 393 K. The calcined materials were characterized using small-angle X-ray scattering (SAXS) and nitrogen and argon adsorption at 77 K. SAXS patterns were generally similar to those reported for FDU-1 silica, indicating the cubic close-packed (Fm3m) structure, but the presence of stacking faults characteristic of a hexagonal close-packed structure cannot be precluded. The addition of the salt was found to significantly narrow the pore size distributions and to improve the uniformity of entrances to the cagelike mesopores, whereas the pore diameter, specific surface area, and pore volume were similar (in most cases slightly lower) to those for FDU-1 silicas obtained in the absence of NaCl. The materials synthesized in the presence of NaCl also appeared to have better resolved SAXS patterns. The feasibility of tailoring the pore cage diameter (from similar to9.5 to 14.5 nm) and pore entrance diameter (from below 4 to similar to8 nm) simply by adjusting the hydrothermal treatment temperature and time was demonstrated, indicating that these simple and convenient ways of structural design of cagelike mesopores are operative in the case of syntheses in the presence of inorganic salts.