Control over the synthesis of monodisperse silica particles up to mesoscopic scale is generally made difficult due to intrinsic limitation to submicrometric dimensions and secondary nucleation in seeded experiments. To investigate this issue and overcome these difficulties, we have implemented single step processing by quantifying the effects of the progressive addition of a diluted tetraethyl orthosilicate solution in ethanol on the size and monodispersity of silica particles. Contrary to particles grown in seeded polymerization, monodisperse particles with size up to 2 mum were synthesized. Moreover, the particles exhibit a final diameter (d(f)), which varies with V-1/3 oven more than 2 orders of magnitude in rate of addition (V). On the basis of a kinetic study in the presence of addition showing that particle growth is limited by the diffusion of monomer species, we developed a diffusion-limited growth model to theoretically explain the observed d(f)(V) behavior and quantitatively retrieve the measured amplitude and exponent. Using a single parameter procedure, we can therefore predict and generate in the room temperature range, monodisperse particles of a targeted size by simply adjusting the rate of addition.