Journal of Colloid and Interface Science, Vol.284, No.1, 71-77, 2005
Determination of surface properties of iron hydroxide-coated alumina adsorbent prepared for removal of arsenic from drinking water
A novel type adsorbent was prepared by in situ precipitation of Fe(OH)3 on the surface of activated Al2O3 as a support material. The iron content of the adsorbent was 0.31 +/- 0.003% m/m (56.1 mmol/g); its mechanical and chemical stability proved to be appropriate in solutions. The total capacity of the adsorbent was 0.12 mmol/g, and the pH of zero point of charge, pH(zpc) = 6.9 +/- 0.3. Depending on the pH of solutions, the adsorbent can be used for binding of both anions and cations, if pH(eq) < pH(zpc) anions are sorbed on the surface of adsorbent (S) through {S-OH2+} and {S-OH} groups. A graphical method was used for the determination of pH(iep) (isoelectric points) of the adsorbent and values of pH(iep) = 6.1 +/- 0.3 for As(III) and pH(iep) = 8.0 +/- 0.3 for As(V) ions were found. The amount of surface charged groups (Q) was about zero within the a pH range of 6.5-8.6, due to the practically neutral surface formed on the adsorption of As(V) ions. At acidic pH (pH 4.7), Q = 0.19 mol/kg was obtained. The adsorption of arsenate and arsenite ions from solutions of 0.1-0.4 mmol/L was represented by Langmuir-type isotherms. A great advantage of the adsorbent is that it can be used in adsorption columns, and low waste technology for removal of arsenic from drinking water can be developed. (c) 2004 Elsevier Inc. All rights reserved.
Keywords:iron hydroxide;alumina;arsenate;arsenite;adsorption;isotherms;zero point of charge;isoelectric points