Polyamide 6 (PA6)/carbon nanotubes (PA6/CNTs) composites have been prepared by in situ polymerization of epsilon-caprolactam in the presence of pristine and carboxylated multi-walled carbon nanotubes (MWNT and MWNTCOOH). Viscosity measurements show that adding 0.5 wt% of carbon nanotubes (CNTs) does not affect the molecular weight of PA6. Compared with pure PA6, the yield strength of PA6/CNTs composites loaded with 0.5 wt% CNTs is almost unchanged, and the tensile strength is increased slightly. Dynamic mechanical analysis (DMA) demonstrates that both the storage modulus (E') and glass transition temperature (T-g) of the PA6/CNTs composites increase, particularly for PA6/MWNTCOOH, indicating there is some chemical bonding between PA6 and MWNTCOOH. Scanning electron microscopy (SEM). transmission electron microscopy (TEM) and ultra small-angle X-ray scattering (USAXS) show that MWNT and MWNTCOOH are well dispersed in PA6 matrix. Comparison of the USAXS data with a stiff-rod model and wormlike rod model reveals that the CNTs are quite flexible, regardless the degree of chemical modification. Due to the flexibility of CNTs, mechanical properties of the PA6/CNTs composites are marginally enhanced. (c) 2005 Elsevier Ltd. All rights reserved.