Synthetic pathways to (salcy)CoX (salcy = N,N'-bis(3,5-di-tert-butylsalicylidene)-1,2-diaminocyclohexane; X = halide or carboxylate) complexes are described. Complexes (R,R)-(salcy)CoCl, (R,R)-(salcy)CoBr, (R,R)-(salcy)CoOAc, and (R,R)-(salcy)CoOBzF(5) (OBzF(5) = pentafluorobenzoate) are highly active catalysts for the living, alternating copolymerization of propylene oxide (PO) and CO2, yielding poly(propylene carbonate) (PPC) with no detectable byproducts. The PPC generated using these catalyst systems is highly regioregular and has up to 99% carbonate linkages with a narrow molecular weight distribution (MWD). Inclusion of the cocatalysts [PPN]Cl or [PPN][OBzF(5)] ([PPN] = bis(triphenylphosphine)iminium) with complex (RR)-(salcy)CoCl, (R,R)-(salcy)CoBr, or (R,R)-(salcy)CoOBzF(5) results in remarkable activity enhancement of the copolymerization as well as improved stereoselectivity and regioselectivity with maximized reactivity at low CO2 pressures. In the case of [PPN]Cl with (R,R)-(salcy)CoOBzF(5), an unprecedented catalytic activity of 620 turnovers per hour is achieved for the copolymerization of rac-PO and CO2, yielding iso-enriched PPC with 94% head-to-tail connectivity. The stereochemistry of the monomer and catalyst used in the copolymerization has dramatic effects on catalytic activity and the PPC microstructure. Using catalyst (R,R)-(salcy)CoBr with (S)-PO/CO2 generates highly regioregular PPC, whereas using (R)-PO/CO2 with the same catalyst gives an almost completely regiorandom copolymer. The rac-PO/CO2 copolymerization with catalyst rac-(salcy)CoBr yields syndio-enriched PPC, an unreported PPC microstructure. In addition, (R,R)-(salcy)CoOBzF(5)/[PPN]Cl copolymerizes (S)-PO and CO2 with a turnover frequency of 1100 h(-1), an activity surpassing that observed in any previously reported system.