The preparation and physical characterization of a poly(vinylidene fluoride)-graft-poly (styrene sulfonic acid) (PVDF-g-PSSA) membrane prepared by a solution-grafting method were described. These membranes exhibited high conductivity with a value 3.22 x 10(-2) S/cm at 30 degrees C. ICP studies revealed that the PVDF-9-PSSA membrane showed dramatically lower vanadium ion permeability compared to Nation 117. Trivalent vanadium ions had the highest permeability through all these membranes in contrast to pentavalent vanadium ions with the lowest. The VRB with the low-cost PVDF-g-PSSA membrane exhibited a higher performance than that with Nafion 117 under the same operating conditions, and its energy efficiency reached 75.8% at 30 mA/cm(2). The performance of VRB with the PVDF-g-PSSA membrane can be maintained after more than 200 cycles at a current density of 60 mA/cm(2).