Copper containing faujasite has been successfully prepared for the first time using a direct synthesis method. Faujasite type zeolite can be prepared in the presence of copper species by tuning the synthesis conditions. Ammonium hydroxide was used to form a copper complex that was later mixed with the reacting gel. Sodium is required to obtain copper faujasite. The complete elimination of sodium ions from the starting gel produces amorphous material. Crystallization took place at 358 K for 11 days. Crystallization temperature of 373 K produces ANA type zeolite as an impurity. Increasing by two times the amount of copper complex added to the reacting gel increases the crystallization time of Cu-FAU from 11 to 20 days (the crystallization rate decreases). The copper containing faujasite obtained was characterized by XRD, FESEM, EDX, EPR, FT-IR, TPR, and BET. According to the XRD pattern only FAU type zeolite was obtained. According to TPR experiments, the reduction temperature for Cu2+ ions present in Cu-FAU prepared by direct synthesis was 70 K more than for Cu-FAU prepared by ion-exchange. This difference can be due to the different location of the copper ions in the supercages or in the sodalite cages of the faujasite. (c) 2005 Elsevier B.V. All rights reserved.