Journal of the Korean Industrial and Engineering Chemistry, Vol.17, No.2, 170-176, April, 2006
Export Citation
폴리카보네이트 판 위에 (3-glycidoxypropyl)trimethoxysilane의 졸-겔 반응을 이용한 하드 코팅
Hard Coatings on Polycarbonate Plate by Sol-Gel Reaction of (3-glycidoxypropyl)trimethoxysilane
김주연, 신영재1, 신연록, 지영존, 윤여성2, 신재섭†
  • 충북대학교 화학과
  • 1한국과학기술원 전자전산학과
  • 2자동차부품연구원
Ju Youn Kim, Young Jae Shin1, Youn Rok Shin, Young Jon Ji, Yeo Seong Yoon2, and Jae Sup Shin†
  • Department of Chemistry, Chungbuk National University, Cheongju, Chungbuk 361-763, Korea
  • 1Department of Electrical Engineering and Computer Science, KAIST, Daejeon, 305-701, Korea
  • 2Korea Automotive Technology Institute, Chonan, Chungnam 330-912, Korea
E-mail:
초록
자동차의 유리를 폴리카보네이트로 대체하기 위하여 폴리카보네이트 판 위에 하드 코팅을 시도하였다. 본 연구에서는 (3-glycidoxypropyl)trimethoxysilane (GPTMS), (3-aminopropyl)triethoxysilane (APS), diethylenetriamine (DETA)으로 부터 졸-겔 과정을 이용하여 코팅을 형성하였는데 이 때 가장 우수한 물성을 갖는 조건들을 찾아보았다. GPTMS와 DETA를 사용하였을 때는 연필 경도 2H의 표면이 매우 고른 코팅을 형성할 수 있었으며 GPTMS와 APS를 사용하였을 때에도 역시 연필 경도 2H의 고른 면을 갖는 코팅을 형성할 수 있었다. 그리고 GPTMS와 DETA를 이용하여 형성한 코팅이 매우 우수한 내마모성을 나타내었다.
The hard coatings on the polycarbonate plate were performed with the object of substitution the glass in the car to the polycarbonate plate. In this research, (3-glycidoxypropyl)trimethoxysilane (GPTMS), (3-aminopropyl)triethoxysilane (APS), and diethylenetriamine (DETA) were used to prepare the coatings by a sol-gel process. The optimum conditions and formulation to achiere the excellent physical properties of the coating were determined. In the case of using GPTMS and DETA, the smooth coating which had the 2 H class in pencil hardness was formed. In the case of using GPTMS and APS, the coating which had the 2 H class in pencil hardness was also formed. And the coatings with GPTMS and DETA showed an excellent abrasion resistant.
Keywords:sol-gel process;hard coating;polycarbonate
  1. Medda SK, Kundu D, De G, J. Non-Cryst. Solids, 318, 149 (2003) 
  2. Yang HS, Kwon OH, Lee JD, Rho JS, Kim YH, J. Korean Ind. Eng. Chem., 7(5), 823 (1996)
  3. Lee YT, Jeong DS, Jeong HJ, Polym.(Korea), 19(6), 753 (1995)
  4. Kim HK, Kim JG, Yu JA, Hong JW, J. Korean Ind. Eng. Chem., 12(3), 287 (2001)
  5. Rats D, Hajek V, Martinu L, Thin Solid Films, 340(1-2), 33 (1999) 
  6. Yoon SE, Woo HG, Kim DP, Polym.(Korea), 24(3), 389 (2000)
  7. Lee TH, Kang ES, Bae BS, J. Sol-Gel Sci. Technol., 27, 23 (2003) 
  8. Eo YJ, Kim DJ, Bae BS, Song KC, Lee TY, Song SW, J. Sol-Gel Sci. Technol., 13, 409 (1998) 
  9. Park DG, Polym. Sci. Technol., 8, 268 (1997)
  10. Hwang DK, Moon JH, Shul YG, Jung KT, Kim DH, Lee DW, J. Sol-Gel Sci. Technol., 26, 783 (2003) 
  11. Lee MS, Jo NJ, J. Sol-Gel Sci. Technol., 24, 175 (2002) 
  12. Chou TP, Cao G, J. Sol-Gel Sci. Technol., 27, 31 (2003) 
  13. Mackenzie JD, Bescher EP, J. Sol-Gel Sci. Technol., 19, 23 (2000)