Modification of chitosan by grafting with 4-vinylpyridine (VP) was carried out both in homogeneous and heterogeneous phases, using potassium persulfate (K2S2O8) and sodium bisulfite (NaHSO3) as redox initiators. The effect of monomer concentration, initiator concentration and redox ratio, time and temperature on the extent of grafting (G%), homopolymer formation, and the efficiency of grafting were studied. Values of grafting percentages up to 96% were reached in heterogeneous conditions and up to 130% in homogeneous conditions (in 5% acetic acid). The grafting was confirmed by FTIR and H-1 NMR spectroscopy. The grafted samples were characterized by scanning electron microscopy, X-ray diffraction, and thermogravimetric analysis. The crystallinity of the used chitosan was not affected by grafting, it even increased slightly. Dye uptake of the grafted samples towards the different types of dyes (acidic and basic) was investigated and was found to im-prove profoundly over the native chitosan with a higher uptake for the acidic dye. The grafted samples showed an increased swelling in water, which increased further upon quaternization of the graft copolymers. The extent of swelling is higher in acidic and basic media more than in neutral pH. The grafted copolymers are soluble with difficulty in warm acetic acid solution. The quaternized graft copolymer was found to be soluble in water. The biological activity of the quaternized graft copolymers (G = 130 and 80%) was investigated and was found to have an inhibition effect on both the Azotobacter fungus and the bacterium Fusarium oxysporium. The effect on the micro organisms is proportional to the amount of VP in the graft copolymer. (c) 2006 Wiley Periodicals, Inc.