Polymer, Vol.47, No.11, 3856-3865, 2006
Dielectric analyses of a series of poly(2-hydroxyethyl methacrylate-co-2,3-dihydroxypropyl methacylate) copolymers
The dielectric spectra of a series of copolymers of 2-hydroxyethyl methacrylate (HEMA) and 2,3-dihydroxypropyl methacrylate (DHPMA) were investigated. Recently, the full range dielectric spectrum of poly(2-hydroxyethyl metbacrylate) was reported. This study looks at the effects on the dielectric behavior as a result of 2,3-dihydroxypropyl methacrylate addition. The dielectric permittivity, epsilon', and the loss factor, epsilon", were measured using a dielectric analyzer in the frequency range of 0.6 Hz to 100 kHz and between the temperature range of -150 and 275 degrees C. The electric modulus formalism was used to reveal the viscoelastic and conductivity relaxations present in the polymers. Several notable changes were observed as 2,3-dihydroxypropyl methacrylate concentration increased. It was observed through DSC and DEA that the glass transition temperature decreased as DHPMA content increased. The secondary dielectric relaxations were also affected as it was recorded that the activation energy for the gamma transition increased and the P relaxation decreased with DHPMA content. Ionic conductivity data prove that DHPMA facilitates ionic mobility more efficiently than HEMA. (c) 2006 Published by Elsevier Ltd.
Keywords:2-hydroxyethyl methacrylate (HEMA);2,3-dihydroxypropyl methacrylate (DHPMA);dielectric relaxation