A new form of LiMn2O4 is reported. The structure is the CaFe2O-type and 6% denser than the spinel. The structure transformation was achieved by heating at 6 GPa. Analysis of the neutron diffraction pattern confirmed an average of the structure; the unit cell was orthorhombic at a = 8.8336(5) angstrom, b = 2.83387(18) angstrom, and c = 10.6535(7) angstrom (Pnma). Electron diffraction patterns indicated an order of superstructure 3a x b x c, which might be initiated by Li vacancies. The exact composition is estimated at Li0.92Mn2O4 from the structure analysis and quantity of intercalated Li. The polycrystalline CaFe2O4-type compound showed semiconducting-like characters over the studied range above 5 K. The activation energy was reduced to similar to 0.27 eV from similar to 0.40 eV at the spinel form, suggesting a possible enhancement of hopping mobility. Magnetic and specific-heat data indicated a magnetically glassy transition at similar to 10 K. As the CaFe2O4-type transition was observed for the mineral MgAl2O4, hence the new form of the lithium manganese oxide would provide valuable opportunities to study not only the magnetism of strongly correlated electrons but also the thermodynamics of the phase transition in the mantle.