A new approach for in situ fabrication of nanoscale fibrous chitosan membrane by biospecific degradation under physiological situation was studied. The chitosan binary blend membranes were fabricated by solvent casting of chitosan solution containing highly deacetylated chitosan (HDC) and moderately deacetylated chitosan (MDC) with different ratio. The biodegradation process was performed in PBS (pH 7.4) containing lysozyme at the temperature of 37 degrees C. Experimental results from weight loss, reducing sugar in surrounding media, FT-IR, X-ray diffraction, gel permeation chromatography (GPC) and SEM throughout the study showed that the biospecific degradation by lysozyme had removed MDC component selectively. When the ratio of MDC in the binary blend membranes amounted to 0.5, nanoscale domains of HDC and MDC were obtained, and thus a nanoscale fibrous structure was fabricated after biospecific degradation of MDC. This nanofibrous structure and the biospecific degradation of chitosan membranes can have potential advantages and interesting implications in tissue engineering and drug delivery. (c) 2006 Elsevier B.V. All rights reserved.