The surface dynamics of adsorbed CO molecules formed by dissociative adsorption of HCHO at a polycrystalline Pt electrode/electrolyte solution interface was studied by picosecond time-resolved sum-frequency generation (TR-SFG) spectroscopy. A SFG peak at 2050-2060 cm(-1) was observed at the Pt electrode in HClO4 solution containing HCHO at 0-300 mV (vs Ag/AgCl), indicating the formation of adsorbed CO at an atop site of the Pt surface as a result of dissociative adsorption of HCHO. The peak position varied with potential by similar to 33 cm(-1)/V, as previously found in an infrared reflection absorption spectroscopy ( IRAS) study. Irradiation of an intense picosecond visible pulse (25 ps, 532 nm) caused an instant intensity decrease and broadening of the CO peak accompanied by the emergence of a new broad peak at similar to 1980 cm(-1) within the time resolution of the system. These results suggest a decrease and increase in the populations of CO adsorbed on atop and bridge sites, respectively, upon visible pump pulse irradiation.