We model nongraphitized carbon black surfaces and investigate adsorption of argon on these surfaces by using the grand canonical Monte Carlo simulation. In this model, the nongraphitized surface is modeled as a stack of graphene layers with some carbon atoms of the top graphene layer being randomly removed. The percentage of the surface carbon atoms being removed and the effective size of the defect ( created by the removal) are the key parameters to characterize the nongraphitized surface. The patterns of adsorption isotherm and isosteric heat are particularly studied, as a function of these surface parameters as well as pressure and temperature. It is shown that the adsorption isotherm shows a steplike behavior on a perfect graphite surface and becomes smoother on nongraphitized surfaces. Regarding the isosteric heat versus loading, we observe for the case of graphitized thermal carbon black the increase of heat in the submonolayer coverage and then a sharp decline in the heat when the second layer is starting to form, beyond which it increases slightly. On the other hand, the isosteric heat versus loading for a highly nongraphitized surface shows a general decline with respect to loading, which is due to the energetic heterogeneity of the surface. It is only when the fluid-fluid interaction is greater than the surface energetic factor that we see a minimum-maximum in the isosteric heat versus loading. These simulation results of isosteric heat agree well with the experimental results of graphitization of Spheron 6 (Polley, M. H.; Schaeffer, W. D.; Smith, W. R. J. Phys. Chem. 1953, 57, 469; Beebe, R. A.; Young, D. M. J. Phys. Chem. 1954, 58, 93). Adsorption isotherms and isosteric heat in pores whose walls have defects are also studied from the simulation, and the pattern of isotherm and isosteric heat could be used to identify the fingerprint of the surface.